Communication: microstructural stability of the ( α + β ) solution-treated and quenched near-α titanium alloy Ti-5.8al-4Sn-3.5Zr-0.70Nb-0.50Mo-0.35Si-0.06C : Ghosal. P., Prasad, R. and Ramachandra, C. Metall. Mater. Trans. A (1995) 26A (10), 2751–2755