The strength-ductility balance of Al 0·4 CoCu 0.6 NiTi x (x≤1.0) and Al 0·4 CoCu 0·6 NiSi 0.2 Ti x (x≤0.5) high entropy alloys by regulating the proportion of Ti and improving the cooling rate