The role of service-induced residual stresses in initiating and propagating stress corrosion cracking (SCC) in a 316 stainless steel pressure-relief-valve nozzle set
Abdul Jawwad, Abdul Kareem, Mahdi, Mofid, Alshabatat, NabeelVolume:
105
Language:
english
Journal:
Engineering Failure Analysis
DOI:
10.1016/j.engfailanal.2019.07.062
Date:
November, 2019
File:
PDF, 2.62 MB
english, 2019